Our tin bath normally (always) looks like milk with a little coffee in it.
Sounds like you're fine. You do probably want to use anode bags though.
Tim Reeves

-----Original Message-----
From: Sean Clinton [mailto:[log in to unmask]]
Sent: Monday, August 27, 2001 12:48 PM
Subject: Tin Plating bath (not clear anymore)


Techneters,

I am bringing up a tin plating bath to replace our tin/lead plating system
for etch resist and have noticed something about our new bath.  Upon
makeup, the bath was clear, albeit a slight butterscotch color.  It has
since become somewhat murky, and looks like its on its way to becoming a
murky coffee and cream color.  I was told this is normal, but I seem to
recall that stannic tin is not soluble in acid tin baths.  Am I converting
the stannous to stannic tin?  If so, will this adversely affect my plating
efficiency?  Basically, is it ok to have a murky looking acid tin bath?  My
plating results using test panels seem to indicate that performance has not
changed.  My plating calculations indicate the efficiency is on the order
of 98-99%.  My vendor says it's ok, but I'd like some other opinions on
this.

Also, the system uses eductors for solution turnover and the pump runs
solution continuously through a polypropylene filter.  I am not using bags
over my anodes (slabs), and I don't have a flow meter on the pump yet, so I
cannot judge the solution turnover rate.  The eductors do move a large
amount of solution  in the tank though.


Thanks,

Sean Clinton
Process Engineer
Proto Engineering Corporation
(408) 737-4136

---------------------------------------------------------------------------------
Technet Mail List provided as a free service by IPC using LISTSERV 1.8d
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt delivery of Technet send the following message: SET Technet NOMAIL
Search previous postings at: www.ipc.org > On-Line Resources & Databases > E-mail Archives
Please visit IPC web site (http://www.ipc.org/html/forum.htm) for additional
information, or contact Keach Sasamori at [log in to unmask] or 847-509-9700 ext.5315
---------------------------------------------------------------------------------