We have our system set for 0.15MOhm-cm as the trip point.
-----Original Message-----
From: Alain Savard [mailto:[log in to unmask]]
Sent: Tuesday, June 05, 2001 11:44 AM
To: [log in to unmask]
Subject: [TN] Minimum requirements for final rinse in assembled boards
Hi netters,
A question from a colleague of mine. Subject: Water soluble flux rinse
water.
What is the minimum water cleanliness level of the final rinse for
assembled/soldered PCB?
Reference?
Thanks a lot,
Alain Savard
CAE Inc.
----------------------------------------------------------------------------
-----
Technet Mail List provided as a free service by IPC using LISTSERV 1.8d
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt delivery of Technet send the following message: SET
Technet NOMAIL
Search previous postings at: www.ipc.org > On-Line Resources & Databases >
E-mail Archives
Please visit IPC web site (http://www.ipc.org/html/forum.htm) for additional
information, or contact Keach Sasamori at [log in to unmask] or 847-509-9700
ext.5315
----------------------------------------------------------------------------
-----
---------------------------------------------------------------------------------
Technet Mail List provided as a free service by IPC using LISTSERV 1.8d
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt delivery of Technet send the following message: SET Technet NOMAIL
Search previous postings at: www.ipc.org > On-Line Resources & Databases > E-mail Archives
Please visit IPC web site (http://www.ipc.org/html/forum.htm) for additional
information, or contact Keach Sasamori at [log in to unmask] or 847-509-9700 ext.5315
---------------------------------------------------------------------------------
|
|
|