Subject:
From:
"<Peter George Duncan>" <[log in to unmask]>
Reply To:
TechNet E-Mail Forum.
Date:
Mon, 28 May 2001 16:27:18 +0800
Content-Type:
text/plain
Parts/Attachments:
text/plain (132 lines)
Hi, Chuck,

I can't answer for the electronic side of your problem, though it does
sound like you have a problem with uncoated boards, humidity and ionic
contamination. You may have to kill one bird with two stones - if you need
to put a barrier coating between the boards and the atmosphere (conformal
coating), you will have to get the boards clean enough for a coating to
stick. If you're using a no-clean soldering process, you will still have to
clean the boards, and by cleaning them sufficiently for conformal coating,
you may find that your ionic contamination problem disappears, in which
case you may choose not to coat.

Coating is good until you need to rework a board, and then it becomes a
pain as it has to be removed and that's usually messy and time-consuming.
However, if coating proves to be your answer, an acrylic varnish such as
Humiseal 1B31 should do the trick. It can be applied by brush, dipping or
spraying, and dries in ambient atmospheric conditions. Make sure the board
is dry before coating.

Pete Duncan





                    Chuck Mays
                    <com@INVETECH        To:     [log in to unmask]
                    .COM.AU>             cc:     (bcc: DUNCAN Peter/Asst Prin Engr/ST Aero/ST Group)
                    Sent by:             Subject:     [TN] Ionic contamination limit for PWA with
                    TechNet              0402 sized components
                    <[log in to unmask]
                    ORG>


                    05/28/01
                    12:04 PM
                    Please
                    respond to
                    "TechNet
                    E-Mail
                    Forum.";
                    Please
                    respond to
                    Chuck Mays






I've checked the technet archive and have not found a similar problem, so
here goes.

I have a problem with a small mobile product that is failing in field
trials.  One area we have considered is a combination of RH and the level
of ionic contamination affecting high impedance areas of the PWA to cause
the problem.  (The problem exhibits itself as a RAM corruption and the S/W
engineers are busily making sure it isn't their problem.)

An external lab checked a sample of the PWA's using the Omega method and
found the average level to be about 18 ug/sq.in.  (I'm aware that 10
ug/sg.in. is the recommended limit.)  The PWA uses 0402 sized resistors and
is the finest pitched assembly that the manufacturer in China who builds
this and other boards for us uses.  A no clean process is used.  The other
products built for us by this manufacturer are OK in terms of ionic
contamination and field performance.

Most of the failures in field trials have occurred not too far from the bay
in one of the suburbs of Sydney where the field trials are in progress.
The temperature is not high (15 - 20 degrees C), but we are now in the
rainy season.  One day, when it rained in the suburb nearer the bay, and
not in the other field trial areas, 6 of the field trial units failed in
the one area.

My questions are:
1.  Does anyone have experience that indicates that the 10ug/sq.in. level
for ionic contamination is OK for PWAs that use 0402 sized components?  Or
does experience indicate that a lower level is more appropriate and if so,
what level?  (It don't know the exact pitch of this board, but am waiting
for the answer.)
2.  Is it possible to determine an impedance above which one should be
concerned with a level of ionic contamination for a given voltage?
3.  If it turns out that for this design, RH and the level of ionic
contamination are causing the problem, can the situation be improved by
conformally coating the board or areas of the board?  (If so, can someone
please point me to the applicable standards for conformal coating?
Thanks.)

Best Regards,

Chuck Mays

Invetech Operation Pty Ltd
[log in to unmask]

Tel 613 9211 7700
Fax 613 9211 7702

The information contained in this message and any attachments is
confidential and intended for the named recipient(s).  If you have received
this message in error, please contact the sender by return e-mail and
destroy the message and any attachments.

Any opinions or undertakings expressed in this message are those of the
individual sender except where the sender expressly and with authority
states them to be the opinions of Invetech.

---------------------------------------------------------------------------------

Technet Mail List provided as a free service by IPC using LISTSERV 1.8d
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt delivery of Technet send the following message: SET
Technet NOMAIL
Search previous postings at: www.ipc.org > On-Line Resources & Databases >
E-mail Archives
Please visit IPC web site (http://www.ipc.org/html/forum.htm) for
additional
information, or contact Keach Sasamori at [log in to unmask] or 847-509-9700
ext.5315
---------------------------------------------------------------------------------

---------------------------------------------------------------------------------
Technet Mail List provided as a free service by IPC using LISTSERV 1.8d
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt delivery of Technet send the following message: SET Technet NOMAIL
Search previous postings at: www.ipc.org > On-Line Resources & Databases > E-mail Archives
Please visit IPC web site (http://www.ipc.org/html/forum.htm) for additional
information, or contact Keach Sasamori at [log in to unmask] or 847-509-9700 ext.5315
---------------------------------------------------------------------------------

ATOM RSS1 RSS2