Subject:	Copper levels in wave solder pot
From:	Susan James <[log in to unmask]>
Reply To:	TechNet E-Mail Forum.
Date:	Wed, 28 Feb 2001 12:07:14 -0600
Content-Type:	text/plain
Parts/Attachments:	text/plain (19 lines)

Gurus,
After having our solder pot analyzed, the copper level is showing .1273.
In July of 1999, the copper level was .120.  We are assuming the copper is
coming from the cut component leads.  My concern is whether or not this is
significant enough to change out the solder.  J-STD-006 specs .08 as
acceptable but I don't know how "bad" .1273 is considered to be.  Any help
is appreciated.
Sue James

---------------------------------------------------------------------------------
Technet Mail List provided as a free service by IPC using LISTSERV 1.8d
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt delivery of Technet send the following message: SET Technet NOMAIL
Search previous postings at: www.ipc.org > On-Line Resources & Databases > E-mail Archives
Please visit IPC web site (http://www.ipc.org/html/forum.htm) for additional
information, or contact Keach Sasamori at [log in to unmask] or 847-509-9700 ext.5315
---------------------------------------------------------------------------------

ATOM RSS1 RSS2

LISTSERV.IPC.ORG