White Tin is an immersion tin process that can have a limited number of
reflow operations because of the very thin nature of the deposit. Does your
supplier guarantee how may reflow cycles to expect
Original investigations by GPT over 4 years ago in the UK showed that Tin
Whiskering was also a problem
-----Original Message-----
From: TechNet [mailto:[log in to unmask]]On Behalf Of Spencer Davis
Sent: 07 February 2001 18:50
To: [log in to unmask]
Subject: [TN] White Tin
We have had similar problems with the White Tin process. There appears to
be an oxide or contaminate that occurs after more than one reflow operation.
This inhibits the solder wetting. We are trying to get to the root cause.
Our CM also recommended HASL for the same reasons. However, we don't feel
that this will yield a planar surface. We are also looking at Immersion
Silver or Nickel/Gold as alternatives. But they may have similar or
different process issues.
Regards,
Spencer
----------------------------------------------------------------------------
-----
Technet Mail List provided as a free service by IPC using LISTSERV 1.8d
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt delivery of Technet send the following message: SET
Technet NOMAIL
Search previous postings at: www.ipc.org > On-Line Resources & Databases >
E-mail Archives
Please visit IPC web site (http://www.ipc.org/html/forum.htm) for additional
information, or contact Keach Sasamori at [log in to unmask] or 847-509-9700
ext.5315
----------------------------------------------------------------------------
-----
---------------------------------------------------------------------------------
Technet Mail List provided as a free service by IPC using LISTSERV 1.8d
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt delivery of Technet send the following message: SET Technet NOMAIL
Search previous postings at: www.ipc.org > On-Line Resources & Databases > E-mail Archives
Please visit IPC web site (http://www.ipc.org/html/forum.htm) for additional
information, or contact Keach Sasamori at [log in to unmask] or 847-509-9700 ext.5315
---------------------------------------------------------------------------------
|
|
|