Jim,
Electro-migration test would be an excellent choice.
Tom Burek



        [log in to unmask]
01/11/01 09:12 AM

        To:     [log in to unmask] @ INTERNET
        cc:
        Subject:        [TN] ROSIN FLUX RESIDUE

We have a design which requires entrapped rosin flux (either R or RMA).
We'd like to perform a quick test to determine if this will cause any
problems.  The question is would it be better to perform 48 hr. salt fog or
10 day temp humidity?  Any other recommendations?  The application is a Navy
aircraft platform.

Thanks,
Jim Marsico
EDO Electronic Systems Group
[log in to unmask] <mailto:[log in to unmask]>

--------------------------------------------------------------------------------
-
Technet Mail List provided as a free service by IPC using LISTSERV 1.8d
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt delivery of Technet send the following message: SET Technet NOMAIL
Search previous postings at: www.ipc.org > On-Line Resources & Databases > E-mail Archives
Please visit IPC web site (http://www.ipc.org/html/forum.htm) for additional
information, or contact Keach Sasamori at [log in to unmask] or 847-509-9700 ext.5315
--------------------------------------------------------------------------------
-

---------------------------------------------------------------------------------
Technet Mail List provided as a free service by IPC using LISTSERV 1.8d
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt delivery of Technet send the following message: SET Technet NOMAIL
Search previous postings at: www.ipc.org > On-Line Resources & Databases > E-mail Archives
Please visit IPC web site (http://www.ipc.org/html/forum.htm) for additional
information, or contact Keach Sasamori at [log in to unmask] or 847-509-9700 ext.5315
---------------------------------------------------------------------------------