Hi Ingemar,
You did not give the thermal history, but to get "Ni/Tin IMC is many microns"
thick you need to sit at high temperatures for a long time--not just one or 2
reflows. Just look up the Ni-dissolution rate in Sn in Klein-Wassink. I would
love to see those pictures together wioth the history.
Werner Engelmaier
---------------------------------------------------------------------------------