Barry
IMHO N2 will not significantly help you with W/S processes. Its major
advantage is to reduce the solids with "no-clean" processes hence lower
visible residues. It will also reduce drossing with wave soldering but
the cost of N2 used is probably more than SnPb saved.
Brian
> Barry Gallegos wrote:
>
> Hey all,
>
> I am looking for a snapshot consensus on the use of nitrogen in the
> assembly process for reflow as well as in wave solder where the flux
> vehicle is organic water soluble flux.
>
> what does it buy me. for the cost. I have no equipment in place
> for nitrogen and my ovens are not even retrofit able. the wave is
> upgradeable but is a Vitronics delta wave that has reduced drossing
> process on it that is using organic water soluble flux.
>
> I am just asking for some industry experts opinions on this process.
>
> I would like to say thank you for any help in advance.
>
> Barry Gallegos, PE
> Western Electronics, LLC
> 110 E. 43rd st. Boise, ID. 83714
> P-208-377-1557
> F-208-377-9836
>
---------------------------------------------------------------------------------
Technet Mail List provided as a free service by IPC using LISTSERV 1.8d
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt delivery of Technet send the following message: SET Technet NOMAIL
Search previous postings at: www.ipc.org > On-Line Resources & Databases > E-mail Archives
Please visit IPC web site (http://www.ipc.org/html/forum.htm) for additional
information, or contact Keach Sasamori at [log in to unmask] or 847-509-9700 ext.5315
---------------------------------------------------------------------------------
|
|
|