TECHNET Archives

September 2000

TechNet@IPC.ORG

Options: Use Monospaced Font
Show Text Part by Default
Condense Mail Headers

Message: [<< First] [< Prev] [Next >] [Last >>]
Topic: [<< First] [< Prev] [Next >] [Last >>]
Author: [<< First] [< Prev] [Next >] [Last >>]

Print Reply
Content-transfer-encoding:
7BIT
Sender:
Subject:
From:
"Meschter, Stephan J" <[log in to unmask]>
Date:
Tue, 5 Sep 2000 09:01:44 -0400
MIME-version:
1.0
Content-type:
text/plain
Reply-To:
"TechNet E-Mail Forum." <[log in to unmask]>, "Meschter, Stephan J" <[log in to unmask]>
Parts/Attachments:
text/plain (54 lines)
        Hi:
        We are presently using electroless Ni/Immersion gold metallization
on our SMT PWBs. Our present requirements are:
>            A.  FINAL FINISH TO BE IMMERSION GOLD PLATING, 10 MICRO INCHES
> THICK
>                   MAXIMUM, OVER 6-9% PHOSPHORUS CONTAINING ELECTROLESS
> NICKEL PLATED
>                   BASE 0.0003 TO 0.0007 INCHES THICK OVER ELECTRO
> DEPOSITED COPPER.
>
One of our PWB suppliers intends to change their Electroless Nickel bath.
The current
phosphorous content of plated nickel is between 6% and 9%. The new bath will
produce phosphorous content between 9% and 12%.

        Reason: The higher phosphorous content prevents occurrences of
"black pad nickel" and also better resist excessive attack on the nickel by
Immersion Gold. So we expect to reduce, or even eliminate, rejections of
product due to excessive gold or for black nickel under gold.

Does the increased phosphorous content eliminate black pad nickel?
Is there going to be an effect on solderability or long term solder joint
life?
Will the PTH barrel become stronger and result in increased stress in the
connections between the inner plane and the PTH?

We are concerned that we may be trading one set of problems for another.

Thanks in advance for any help you can offer.




Steph

Stephan Meschter               [log in to unmask]
Lockheed Martin Control Systems  Phone  :(607)770-2332
600 Main Street, MD R52F         FAX    :(607)770-2056
Johnson City, NY 13790-1888      MARCALL: 8 * 255-2332

##############################################################
TechNet Mail List provided as a free service by IPC using LISTSERV 1.8d
##############################################################
To subscribe/unsubscribe, send a message to [log in to unmask] with following text in
the body:
To subscribe:   SUBSCRIBE TECHNET <your full name>
To unsubscribe:   SIGNOFF TECHNET
##############################################################
Please visit IPC web site (http://www.ipc.org/html/forum.htm) for additional
information.
If you need assistance - contact Keach Sasamori at [log in to unmask] or
847-509-9700 ext.5315
##############################################################

ATOM RSS1 RSS2