Subject:
From:
Roberts Jon <[log in to unmask]>
Reply To:
TechNet E-Mail Forum.
Date:
Wed, 23 Aug 2000 06:52:02 -0500
Content-Type:
text/plain
Parts/Attachments:
text/plain (96 lines)
Added notes.  If you do decided to empty the pot and thoroughly clean the
pot and the elements as one mentioned, the walls of the pot is where the
contaminants (gold, etc) collect over the years and from what I have been
told is worth $ in recycling.  Might ask some companies who reclaim solder.
Has anyone else knows or have heard about this?  I had the pleasure of
working for an individual who been in the industry a very long time
including the early beginnings of NASA and now consults with companies all
over the world.  He said we have forgotten what the walls of the pot really
look like when they are cleaned (scrapped).  I thought I would just mention
this so as not to be forgotten.  Also if a new machine is in the future,
make sure planning is done for no lead solder which is probably going to
affect solder temperatures from what little I have learned so far.  Again my
2 cents worth.  Jon

 -----Original Message-----
From:   Hinners Hans Civ WRALC/LYPME [mailto:[log in to unmask]]
Sent:   Tuesday, August 22, 2000 2:32 PM
To:     [log in to unmask]
Subject:        [TN] Wave Flow Solder Problem

Hi Everybody,

I've been asked to troubleshoot a BIG problem with our wave flow soldering
machine and I could use some advice.  I'm in the beginning stages of
learning about wave flow soldering.

We use Tin Lead 63/37 solder with Kester-5738 Dross Inhibiting Oil and, to
date, my solder analysis has come back fine.
And recently, we've been getting alot of bridging on assemblies (multilayer
FR-4).  No surprise really, there is an embarrassing amount of scum
(dross-?) and our Tinning oil is gunking up.  We've only used this oil for a
few months so it's the only reported process change.  The joints look It's
an old Hollis machine (bought in '83) that has seen better days.  The first
thing management said was, "Should we go and buy a new machine?"  Showed
Kester the pics and they said the oil was at the end of its life and broke
down.

I threw a couple of pictures on my public drive starting with the word
'Solder -'.  I kept them fairly large (~500 k each) so people can get a good
idea of what I'm up against.  For the digital buffs, they're scaled down 60%
from the originals using a Sony DSC-D700 camera.

http://www.driveway.com/share?sid=a8f3cb1d.96df8&name=Pictures

Thoughts, questions, suggestions, . . . . prayers?

Do we just need to scoop the gunk out (that was my weekend) and keep going?
Start over with a fresh bath of solder?


The more I do, the more I learn . . . the hard way.

Hans

~~~~~~~~~~~~~~~~~~~
Hans M. Hinners
Materials Engineer (Process & Manufacturing)
Warner Robins Air Logistics Center
Avionics Production Division
Manufacturing Branch
380 Second Street, Suite 104
Building: 640, Mail Stop: LYPME
Robins AFB, GA 31098-1638
Voice: (478) 926 - 1970 Fax: (478) 926 - 7164
mailto:[log in to unmask]
http://www.robins.af.mil

##############################################################
TechNet Mail List provided as a free service by IPC using LISTSERV 1.8c
##############################################################
To subscribe/unsubscribe, send a message to [log in to unmask] with following
text in
the body:
To subscribe:   SUBSCRIBE TECHNET <your full name>
To unsubscribe:   SIGNOFF TECHNET
##############################################################
Please visit IPC web site (http://www.ipc.org/html/forum.htm) for additional
information.
If you need assistance - contact Keach Sasamori at [log in to unmask] or
847-509-9700 ext.5315
##############################################################

##############################################################
TechNet Mail List provided as a free service by IPC using LISTSERV 1.8c
##############################################################
To subscribe/unsubscribe, send a message to [log in to unmask] with following text in
the body:
To subscribe:   SUBSCRIBE TECHNET <your full name>
To unsubscribe:   SIGNOFF TECHNET
##############################################################
Please visit IPC web site (http://www.ipc.org/html/forum.htm) for additional
information.
If you need assistance - contact Keach Sasamori at [log in to unmask] or
847-509-9700 ext.5315
##############################################################

ATOM RSS1 RSS2