Roger Bilham <[log in to unmask]>
Reply To:
Leadfree Electronics Assembly E-Mail Forum.
Date:
Tue, 1 Aug 2000 18:06:23 +0100
Content-Type:
text/plain
Parts/Attachments:
text/plain (154 lines)
Brian,

As you say, the cover photo is excellent.

To my eye, the solder surface roughness appears worse than it really is
as it seems to be covered, at least in part, by a layer of flux residue
which has craze cracks. These show up best between the toe of the leg
and the top of the adjacent solder and on the circuit board beyond the
left hand end of the pad, i.e. where there is no solder at all.

Of course in the real world, this is how some joints will present
themselves but I wonder what the joint would look like with the residue
removed.

Roger

In message <[log in to unmask]>, Brian Ellis
<[log in to unmask]> writes
>Dave
>
>Compare your results with the excellent cover photo of Soldering & Surface Mount
>Technology Volume 12 Number 2 (2000) which has the caption SnAgCu soldered SOIC
>joint showing typical surface roughness. I think you may find that high Sn
>alloys are just simply more light-diffractive than near-eutectic SnPb ones.
>Notwithstanding, you seem to be changing two parameters (alloy and flux type) at
>the same time. It may be better to change just one, so that you can isolate
>which is causing you grief. Also, may I suggest a metallographic section of such
>a 'faulty' joint to see whether it has bonded well?
>
>Brian
>
>Dave Crabbe wrote:
>
>> As a new member I wonder if a news list wouldn't
>> be a better avenue. I hope the following has not
>> already been discussed and answered.
>>
>> The goal:
>> ===========
>> Finding a lead-free solder paste for use in
>> SMD rework using PACE hot air workstations,
>> in an educational setting.
>>
>> The problem:
>> ===========
>> I've experiemented very briefly with a sample
>> of solder from EFD which consists of Sn96Ag4
>> "no clean, low residue" paste for its suitability
>> in a Community College soldering program
>> contained within a Computer Technician program.
>>
>> I am looking to use the lead-free paste to replace RMA
>> eutectic paste which we use when teaching
>> installation and removal of 1206, 0805, SOT23, SOICs and
>> PLCC installation using a PACE
>> MBT250 hot air jet soldering station.
>>
>> When I used this paste I noticed some characteristics
>> which would seem to make it unsuitable for
>> my application.
>>
>> 1. The solder seems to melt fine with the hot air
>> jet. The jet is normally set to 900 deg F for eutectic
>> paste use and this works fine for melting the lead-free
>> paste sample I have. (900 deg F translates MUCH
>> lower when it reaches the components.) So the
>> higher melting point does not seem to be a problem
>>
>> 2. When the joint cools, it appears dull and grainy.
>> If this were a eutectic joint, it would fail a visual
>> inspection as it would look like the joint were
>> reheated, overheated, or vibrated during solidification.
>>
>> 3. Wetting action seems minimal. I do not get anywhere
>> near the nice wetting action of eutectic solder. Although
>> it appears barely acceptable for 1206 and 0805 packages,
>> it is horrible for SOIC (gullwing) types. It does not seem to
>> bond well with the lead, and the leads seem to set more
>> on top of the solder rather than "sink" down to the pad
>> with the paste wetting all around the lead. At many points
>> the lead/paste junction looks similar to that on a "cold"
>> joint, although in prying the lead / pad apart, it does seem
>> that an intermetallic bond has formed.
>>
>> I have tried various slow heating stages thinking that the
>> leads were not hot enough, but there was no improvement
>> in the end result.
>>
>> Comments & recommendations?
>> ============================
>> Has anyone successfully used any lead-free paste that
>> gives results similar to eutectic? If so, could you list
>> the actual product and manufacturer so that I could get
>> a sample and test for its suitability in our program.
>>
>> Any comments appreciated.
>>
>> Thanks
>>
>> Dave
>>
>> ==========================
>> Dave Crabbe, Faculty
>> Computer Technician Program
>> N.S.C.C - Burridge Campus
>> 372 Pleasant St, Yarmouth, N.S., B5A 2L2
>> http://cst.burridge.nscc.ns.ca/cst
>>
>> ################################################################
>> Leadfree E-Mail Forum provided as a free service by IPC using LISTSERV 1.8c
>> ################################################################
>> To subscribe/unsubscribe, send a message to [log in to unmask]
>> with following text in the body:
>> To subscribe:   SUBSCRIBE Leadfree <your full name>
>> To unsubscribe:   SIGNOFF Leadfree
>> ###############################################################
>> Please visit IPC's Center for Lead-Free Electronics Assembly
>> (http://www.leadfree.org ) for additional information.
>> For technical support contact Keach Sasamori [log in to unmask] or 847-790-5315.
>> ################################################################
>
>################################################################
>Leadfree E-Mail Forum provided as a free service by IPC using LISTSERV 1.8c
>################################################################
>To subscribe/unsubscribe, send a message to [log in to unmask]
>with following text in the body:
>To subscribe:   SUBSCRIBE Leadfree <your full name>
>To unsubscribe:   SIGNOFF Leadfree
>###############################################################
>Please visit IPC's Center for Lead-Free Electronics Assembly
>(http://www.leadfree.org ) for additional information.
>For technical support contact Keach Sasamori [log in to unmask] or 847-790-5315.
>################################################################

--
Roger Bilham
Roger Bilham Consultancy
Tel: +44 (0)20 8467 8819
Fax: +44 (0)8700 548 613
Mobile +44 (0)7 941 122 446

################################################################
Leadfree E-Mail Forum provided as a free service by IPC using LISTSERV 1.8c
################################################################
To subscribe/unsubscribe, send a message to [log in to unmask]
with following text in the body:
To subscribe:   SUBSCRIBE Leadfree <your full name>
To unsubscribe:   SIGNOFF Leadfree
###############################################################
Please visit IPC's Center for Lead-Free Electronics Assembly
(http://www.leadfree.org ) for additional information.
For technical support contact Keach Sasamori [log in to unmask] or 847-790-5315.
################################################################

ATOM RSS1 RSS2