I believe tin simply oxidizes before lead.
Timothy Reeves
|-----Original Message-----
|From: Lou Hart [mailto:[log in to unmask]]
|Sent: Monday, August 21, 2000 9:36 AM
|Subject: tin depletion
|
|
|TechNetters, is tin preferentially depleted from the solder
|pot in wave soldering? If so, what is the mechanism? My
|recollection is that I learned some months back that, left
|unadjusted, tin content of a solder pot will slowly drop.
|Thanks for any comments.
|
|Lou Hart
|
##############################################################
TechNet Mail List provided as a free service by IPC using LISTSERV 1.8c
##############################################################
To subscribe/unsubscribe, send a message to [log in to unmask] with following text in
the body:
To subscribe: SUBSCRIBE TECHNET <your full name>
To unsubscribe: SIGNOFF TECHNET
##############################################################
Please visit IPC web site (http://www.ipc.org/html/forum.htm) for additional
information.
If you need assistance - contact Keach Sasamori at [log in to unmask] or
847-509-9700 ext.5315
##############################################################
|
|
|