Hi all!
Been trying to dial a profile in on the wave today with a board that's fairly
thick, probably around .090", polyimide, all PTH with a fair amount of the
IC's being ceramic. We use a spray fluxer and a RMA flux.
The first boards have been coming off without the preferred topside fillets
at a number of locations. I've been playing with the pre-heat, belt speed,
and even did something that I don't like to do, which was to flux the topside
of the board.
All to no avail...I still had quite a few places that didn't have topside
fillets, and that is something that doesn't go over well here at all.
I started noticing that the places that didn't have topside fillets were at
the same locations. So I came back to my 'pooter and looked at the gerber for
the board. What's really weird was that everyplace there's a thermal for a
pin is where I have no topside fillet??? I thought that thermals were
supposed to help prevent that from happening? But it's true, every single
place there is a thermal= no top solder. Has anybody ever seen that before?
-Steve Gregory-
##############################################################
TechNet Mail List provided as a free service by IPC using LISTSERV 1.8c
##############################################################
To subscribe/unsubscribe, send a message to [log in to unmask] with following text in
the body:
To subscribe: SUBSCRIBE TECHNET <your full name>
To unsubscribe: SIGNOFF TECHNET
##############################################################
Please visit IPC web site (http://www.ipc.org/html/forum.htm) for additional
information.
If you need assistance - contact Keach Sasamori at [log in to unmask] or
847-509-9700 ext.5315
##############################################################
|
|
|