My understanding is that heating FR-4 above its Tg does permanently change
the material (unlike the same process for a thermoplastic, where the
hydrogen bonds re-form, some covalent bonds in a thermoset like epoxy are
irreversibly broken upon heating above Tg), but my own experience is that
the change for any one excursion is small, and that you can do it a few
times without significantly changing the properties of the laminate.
Tim Reeves

-----Original Message-----
From: michael [mailto:[log in to unmask]]
Sent: Wednesday, July 12, 2000 7:15 PM
Subject: Re: Glass Transition Temperature (Tg) Questions


Epoxies are thermosetting. Surely this process is not indefinitely two-way?
Or
should I say: beyond what temperature is the process no longer two-way (and
what
is the technical term for this temp.)?

Michael Fennema

##############################################################
TechNet Mail List provided as a free service by IPC using LISTSERV 1.8c
##############################################################
To subscribe/unsubscribe, send a message to [log in to unmask] with following text in
the body:
To subscribe:   SUBSCRIBE TECHNET <your full name>
To unsubscribe:   SIGNOFF TECHNET
##############################################################
Please visit IPC web site (http://www.ipc.org/html/forum.htm) for additional
information.
If you need assistance - contact Keach Sasamori at [log in to unmask] or
847-509-9700 ext.5315
##############################################################

ATOM RSS1 RSS2