Hi, Nancy,

You may need to use a VERY active flux to solder nickel, such as an amine hydrochloride activated water-soluble type, of course followed by a wash.

Brian

Nancy Trumbull wrote:

> Hi everyone,
>   I've not been on for awhile.  We have been doing trial runs for a new product. Then I missed placed my brain and hurt myself by falling out of a hammock.  Yes, I know it sounds backwards doesn't it.
> Any way I'm  hoping that this finds all of you  health and happy. Because believe me it only takes one study mistake to end it all.
>
> Now  My Question : Sorry if this has already been addressed.
> More than likely most or all of you  have been using these parts.
> But this is our first notices of the change over..
> Our supplier of condenser / ceramic chips has informed us of a coming change.
> They are telling us that they are changing some of the condenser / ceramic chip from palladium to nickel.
> I have looked up the different between the  element and properties.
> in my handy little Thomas Pocket ref.  So I can see the  difference in numbers under elements
> .  And I have noted the difference in the density, Melting and boiling points.
> But I have to be honest It does not mean diddle squat to me.
> So I have a lot of questions and need a lot of help.
>    As
>            1. Performance durability
>            2. Structural difference that might give us issues now and in the further.
>            3. The reliability of the part it is worst or better.
>            4. Are these parts already out there ,  so I really have no worried at all.
>
> If someone would be so kind to give me items that I do or
> don't need to worried about , with reason why. I will greatly appreciate it.
> My understanding is this is all happening because of the availability of palladium and cost.
> I thank all of you for taking the time to read my e-mail and those of you that can and will help me out.
> Nancy T.
>
> ##############################################################
> TechNet Mail List provided as a free service by IPC using LISTSERV 1.8c
> ##############################################################
> To subscribe/unsubscribe, send a message to [log in to unmask] with following text in
> the body:
> To subscribe:   SUBSCRIBE TECHNET <your full name>
> To unsubscribe:   SIGNOFF TECHNET
> ##############################################################
> Please visit IPC web site (http://www.ipc.org/html/forum.htm) for additional
> information.
> If you need assistance - contact Keach Sasamori at [log in to unmask] or
> 847-509-9700 ext.5315
> ##############################################################

##############################################################
TechNet Mail List provided as a free service by IPC using LISTSERV 1.8c
##############################################################
To subscribe/unsubscribe, send a message to [log in to unmask] with following text in
the body:
To subscribe:   SUBSCRIBE TECHNET <your full name>
To unsubscribe:   SIGNOFF TECHNET
##############################################################
Please visit IPC web site (http://www.ipc.org/html/forum.htm) for additional
information.
If you need assistance - contact Keach Sasamori at [log in to unmask] or
847-509-9700 ext.5315
##############################################################