Subject:
From:
Franklin D Asbell <[log in to unmask]>
Reply To:
TechNet E-Mail Forum.
Date:
Thu, 8 Jun 2000 14:14:29 -0500
Content-Type:
text/plain
Parts/Attachments:
text/plain (50 lines)
Sounds like moisture in the fab...

How are they being baked prior to assembly?

Franklin




Barry Gallegos wrote:

> Dear Sirs, Madams, Guru’s.
>
> I have an assembly that we processed thru SMT and then thru the wave
> solder operations. Wave solder flux was with Alpha metals 856
> water-soluble. The assembly is exhibiting a white cloudy / milky
> appearance that looks almost as if the laminate/solder mask has
> changed color. No matter how much we wash this assembly, it will not
> go away.
>
> Is this due to possible moisture in, around or under the solder mask /
> laminate. What is it andis it acceptable.
>
>
> Any advice would be appreciated.
>
>
> Yours truly, (wana-be guru.)
>
> Barry Gallegos
>
> Western Electronics.
>
> 208-377-1557
>

##############################################################
TechNet Mail List provided as a free service by IPC using LISTSERV 1.8c
##############################################################
To subscribe/unsubscribe, send a message to [log in to unmask] with following text in
the body:
To subscribe:   SUBSCRIBE TECHNET <your full name>
To unsubscribe:   SIGNOFF TECHNET
##############################################################
Please visit IPC web site (http://www.ipc.org/html/forum.htm) for additional
information.
If you need assistance - contact Keach Sasamori at [log in to unmask] or
847-509-9700 ext.5315
##############################################################

ATOM RSS1 RSS2