Do you want to measure the total quantities? If so, just dissolve all the residues in
whichever solvent is best for your particular type of flux. You then evaporate the
solvent at a lowish temperature in a weighed beaker and weigh the solid residues +
beaker. The difference is the weight from your sample, which you can then translate as
weight per unit area.. This won't tell you much, though.

Brian

Poh Kong Hui wrote:

> Hi all Technetters,
>
> I would like to know is there any way to measure the flux
> residue that left on the board, after wave-soldering process.
>
> Thanks in advance.
>
> Regards,
> Poh
>
> ##############################################################
> TechNet Mail List provided as a free service by IPC using LISTSERV 1.8c
> ##############################################################
> To subscribe/unsubscribe, send a message to [log in to unmask] with following text in
> the body:
> To subscribe:   SUBSCRIBE TECHNET <your full name>
> To unsubscribe:   SIGNOFF TECHNET
> ##############################################################
> Please visit IPC web site (http://www.ipc.org/html/forum.htm) for additional
> information.
> If you need assistance - contact Keach Sasamori at [log in to unmask] or
> 847-509-9700 ext.5315
> ##############################################################

##############################################################
TechNet Mail List provided as a free service by IPC using LISTSERV 1.8c
##############################################################
To subscribe/unsubscribe, send a message to [log in to unmask] with following text in
the body:
To subscribe:   SUBSCRIBE TECHNET <your full name>
To unsubscribe:   SIGNOFF TECHNET
##############################################################
Please visit IPC web site (http://www.ipc.org/html/forum.htm) for additional
information.
If you need assistance - contact Keach Sasamori at [log in to unmask] or
847-509-9700 ext.5315
##############################################################