Hi Van,
Of course you can apply solder paste on CN pad and run through Reflow.
But you should pay attention some matters:
- Which side of PCB are CNs on? Your CNs should through Reflow only one
time.
- Solder paste may pass the hole and stick on the surface of supporting
plate of Printer, so you can exchange the supporting plate by supporting
pin.
- solder paste amount should be enough to decrease re-touch by solder iron.
I will attach our stencil specification of stencil opening for CN pad.
Please refer.
Bye
----- Original Message -----
From: Van Hoang Dinh <[log in to unmask]>
To: <[log in to unmask]>
Sent: Tuesday, April 11, 2000 5:01 AM
Subject: [TN] THROUGH HOLE CONNECTOR?
> HI ALL,
> ANYONE HAVE EXPERIENCE ON USING THROUGH HOLE CONNECTORS AT REFLOW OVEN?
>
> I MEAN IS : I BUILT A CIRCUIT BOARD WITH ALMOST OF THE PARTS ARE SMT
(DOUBLE
> SIDES REFLOW),
> BUT THERE ARE 2 THROUGH HOLE CONNECTORS HAVE TO BE FIT ON. THEREFORE WE
HAVE
> TO HAND SOLDER THOSE CONNECTORS( TAKE LONG TIME).
> I HAVE BEEN THINKING OF DEPOSITE SOLDER PASTE ON TOP OF CONNECTORS
PAD(RING
> PADS) AND RUN THROUGH REFLOW.
>
> IF WE CAN
> WHAT SHOULD THE APERTURE SHAPE AND SIZE ON THE STENCIL OF THESE CONNECTORS
> PADS?
>
> THANKS,
> VAN
>
> ##############################################################
> TechNet Mail List provided as a free service by IPC using LISTSERV 1.8c
> ##############################################################
> To subscribe/unsubscribe, send a message to [log in to unmask] with
following text in
> the body:
> To subscribe: SUBSCRIBE TECHNET <your full name>
> To unsubscribe: SIGNOFF TECHNET
> ##############################################################
> Please visit IPC web site (http://www.ipc.org/html/forum.htm) for
additional
> information.
> If you need assistance - contact Keach Sasamori at [log in to unmask] or
> 847-509-9700 ext.5315
> ##############################################################
|
|
|