Hi Steve,

now that's intersting!

Sure, the stencil opening must be smaller then the pads. But when you make
them triangular isn't there too little paste on the pads? We work with
0.15mm thick steel stencils and the amount of paste is already very low.

What CAD program can generate such shape stencils automatically?

regards

Jens Behrens



><< Ok..so what are the causes of solder beads?? >>
>
>Hi Jan!
>
>Solder beads or "Squeeze balls" as they're sometimes referred to, are caused
>by too much of the gray stuff...solder paste. In a cleaning environment
>they're usually not a problem because they wash off. But in a no-clean
>environment, BIG headache!
>
>They can be eliminated by modifying the apertures in your stencil to reduce
>the volume of paste you're putting down. Instead of square apertures you can
>turn them into triangles or "homeplates" with the pointy ends pointing
>towards each other to the center of the footprint. A lot of  stencil vendors
>will do this automatically...at least mine does. I just tell them I want
>no-clean apertures for all the passives...I think it's an extra $25-50 charge
>for the editing they have to do in the gerber.
>
>Hope this helps...
>
>-Steve Gregory-

##############################################################
TechNet Mail List provided as a free service by IPC using LISTSERV 1.8c
##############################################################
To subscribe/unsubscribe, send a message to [log in to unmask] with following text in
the body:
To subscribe:   SUBSCRIBE TECHNET <your full name>
To unsubscribe:   SIGNOFF TECHNET
##############################################################
Please visit IPC web site (http://www.ipc.org/html/forum.htm) for additional
information.
If you need assistance - contact Gayatri Sardeshpande at [log in to unmask] or
847-509-9700 ext.5365
##############################################################