<< What is the recommended surface finish for a backplane of .156" thickness
with the press-fit hole size of .024" -.002"/+.003"?
Ken,
IMHO, I can think of two possible reasons why they are suggesting gold. One
is, depending on your board design, that they do not want to subject the
board to the thermal shock of the HSAL finish. The second is that with the
high aspect ratio of your holes they might have trouble holding the
tolerances you are asking for in a HASL finish.
Larry Tawyea
I was suggesting HASL but our backplane house want Gold plating. No fine
pitch parts are on the board. Any obvious reasons for asking Ni-Gold plating?
re,
ken patel >>
##############################################################
TechNet Mail List provided as a free service by IPC using LISTSERV 1.8c
##############################################################
To subscribe/unsubscribe, send a message to [log in to unmask] with following text in
the body:
To subscribe: SUBSCRIBE TECHNET <your full name>
To unsubscribe: SIGNOFF TECHNET
##############################################################
Please visit IPC web site (http://www.ipc.org/html/forum.htm) for additional
information.
If you need assistance - contact Gayatri Sardeshpande at [log in to unmask] or
847-509-9700 ext.5365
##############################################################
|
|
|