Jeffery Harry, would you please expand on the "major problems" you
have seen by running Entek 106 in a dip mode.
Peter Blokhuis
PC World
[log in to unmask]
----------------------------------------------------------------------
If you use Entec 106, make sure that the PCB supplier has an in-line
process. Dip tanks will cause major problems. Also the PCBS need to
be thoroughly dried before packaging. If not, you will have
solderability problems.
Jeffrey_Harry @ 3mail.3com.com@ ugate
----- Previous Message
----------------------------------------------------
To: Technet @ ipc.org @ UGATE
cc:
From: EHolton @ vines.etn.com @ UGATE Date: Thursday October 31,
1996 02:40 PM Subject: OSP Coating
----------------------------------------------------------------------
----------
----------------------------------------------------------------------
---------- ------------------------------
Fellow technetters:
My company is beginning its research into the wonderful world of
organic solderability preservative coatings. Our goal being to
implement this on the circuit boards in the near future. I am looking
for any and all information that anyone may have....
***************************************************************************