The problems I see is that you have to overheat the solder to get a good
flow. The actual temps, you have to experience from what I know.
Jason
Please respond to "TechNet E-Mail Forum."
<[log in to unmask]>; Please respond to Greg
Kilinski <[log in to unmask]>
To: [log in to unmask]
cc: (bcc: Jason Smith)
bcc: Jason Smith
Subject: [TN] Wave Soldering with Sn10
Does anyone have experience wave soldering with Sn10/Pb90 solder?
My
concern is the plastic (non-eutectic) melting range of 268-302 C
(514-576 F), which may cause sluggish solder flow. Are there any
other
areas of concern?
Thanks in advance.
[log in to unmask]
################################################################
TechNet E-Mail Forum provided as a free service by IPC using LISTSERV 1.8c
################################################################
To subscribe/unsubscribe, send a message to [log in to unmask] with following
text in the body:
To subscribe: SUBSCRIBE TechNet <your full name>
To unsubscribe: SIGNOFF TechNet
################################################################
Please visit IPC web site (http://jefry.ipc.org/forum.htm) for additional
information.
For technical support contact Hugo Scaramuzza at [log in to unmask] or
847-509-9700 ext.312
################################################################
################################################################
TechNet E-Mail Forum provided as a free service by IPC using LISTSERV 1.8c
################################################################
To subscribe/unsubscribe, send a message to [log in to unmask] with following text in the body:
To subscribe: SUBSCRIBE TechNet <your full name>
To unsubscribe: SIGNOFF TechNet
################################################################
Please visit IPC web site (http://jefry.ipc.org/forum.htm) for additional information.
For technical support contact Hugo Scaramuzza at [log in to unmask] or 847-509-9700 ext.312
################################################################