Ron,
please could you tell me what flux and solder paste you use in your application?
Thanks,
Gaby

"Hollandsworth, Ron" wrote:

> Scott:
>
> We sampled White Immersion Tin finish on some boards and to date no
> problems.  Class 3 product, Military, Communication gear.  No assembly
> issues, SMT, or thru hole.  Boards were a mixed technology.  All is well so
> far.  Boards are in units in extended stress testing, have been for sometime
> now with no failures yet.
>
> Ron Hollandsworth
> ITT A/CD
>
> ##############################################################
> TechNet Mail List provided as a free service by IPC using LISTSERV 1.8c
> ##############################################################
> To subscribe/unsubscribe, send a message to [log in to unmask] with following text in
> the body:
> To subscribe:   SUBSCRIBE TECHNET <your full name>
> To unsubscribe:   SIGNOFF TECHNET
> ##############################################################
> Please visit IPC web site (http://www.ipc.org/html/forum.htm) for additional
> information.
> If you need assistance - contact Keach Sasamori at [log in to unmask] or
> 847-509-9700 ext.5315
> ##############################################################

##############################################################
TechNet Mail List provided as a free service by IPC using LISTSERV 1.8c
##############################################################
To subscribe/unsubscribe, send a message to [log in to unmask] with following text in
the body:
To subscribe:   SUBSCRIBE TECHNET <your full name>
To unsubscribe:   SIGNOFF TECHNET
##############################################################
Please visit IPC web site (http://www.ipc.org/html/forum.htm) for additional
information.
If you need assistance - contact Keach Sasamori at [log in to unmask] or
847-509-9700 ext.5315
##############################################################