Greetings. We are running into a situation on Lead Free processed PCBs.
Failure mode is finding open vias during unit testing (fully populated).
Boards are Tg170, Material type EM320, 0.063" thick boards.
6 layers of 1 oz copper. ENIG 3~5u"
Suspect vias go from top layer to bottom layer only.
After running through reflow, we have found vias open. No visual signs of
delamination, however when ohming out the via, if we press on the via we get
continuity - thus we suspect the vias are opening during the process.
Anyone out there having these problems, or information concerning this
failure mode? Z-expansion failure?
Tom Parkinson
Quality System Manager - CIT
WinTronics, Inc.
Phone: 724-981-5770 - extension 235
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------
|
|
|