Hope someone can answer this ... how long will parts plated with tin/lead
remain solderable using regular tin/lead solder & RMA flux? These are
metal parts - copper, brass and aluminum. Brass & aluminum have nickel
underplate. My supplier is telling me 12 months @ normal storage
conditions but my captive shop guy is saying "no way"...who's right?
Thanks!
Sheila Smith
Marconi AES
##############################################################