Ken,
Tough question without more details. The best setup depends upon a number of factors including but not limited to the following:
PWB surface finish
PWB thickness (heat sink properties)
Component surface finish
Are you using additional liquid flux or just flux cored solder wire
Solder alloy being added
Ease of cleaning soldered area
Type of cleaning used (cleaning media and hand or machine process)
Post Soldering Ionic Cleanliness requirements
Post Soldering Non-Ionic Cleanliness requirements
I can go on but you get the idea.
Provide more details and you should get the response you desire.
Regards,
Tom Carroll, CQA, CIT, FAA ODA Unit Member
Supplier Quality Engineer
Boeing Defense, Space and Security - East Region Supplier Quality
Currently on Short Term International Assignment for BCA in Sweden
eFAX: 314-777-1845
Cell: 215-692-2463
Softphone Phone Number: 314-545-2358
Saab Sweden Phone: +46 (0)13 185972
Sweden Cell Phone (In Sweden): 0700 945414
Sweden Cell Phone (Outside of Sweden): +46 700 945414
email: [log in to unmask]
P Go Green! Please do not print this e-mail unless necessary.
>NOTE: This communication may contain privileged or other confidential information. If you are not the intended recipient, or believe you have received this communication in error, please do not print, copy, retransmit, disseminate, or otherwise use the information. Also, please indicate to the sender that you have received this e-mail in error, and delete the copy you received. Thank you.
>EXPORT COMPLIANCE STATEMENT:
>"The information contained herein is or may be controlled by the International Traffic in Arms Regulations (ITAR), 22 CFR 120-130, and may not be exported, or disclosed to a foreign person, whether in the United States or abroad, without prior U.S. Government written approval"
-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of Kenneth Wood
Sent: Monday, September 06, 2010 2:30 PM
To: [log in to unmask]
Subject: [TN] Hand Soldering
Hi all.
What is the best setup for hand soldering as far as solder / cleaner?
Rosin core? Water soluble? No-Clean?
What cleaner too?
I've been using rosin core with various cleaners but I have a hard time with the white residue the cleaners leave.
Thanks
Ken
______________________________________________________________________
This email has been scanned by the MessageLabs Email Security System.
For more information please contact helpdesk at x2960 or [log in to unmask] ______________________________________________________________________
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0 To unsubscribe, send a message to [log in to unmask] with following text in the BODY (NOT the subject field): SIGNOFF Technet To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL) To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest Search the archives of previous posts at: http://listserv.ipc.org/archives Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------
______________________________________________________________________
This email has been scanned by the MessageLabs Email Security System.
For more information please contact helpdesk at x2960 or [log in to unmask]
______________________________________________________________________
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------
|