You need to be concerned about more than just the EMF differences. Be careful
of
the area effect. Making the surface more noble, and therefore more corrosion
resistant, is only effective as long as the coating is continuous and intact.
Any small defect, that will inevitably develop, causes and accelerated attack
on
the aluminum, since its small exposed area is now linked to a much larger more
noble surface.
Andy Magee - Applications Engineer
Rogers - Circuit Materials
Tel: (602) 917-5237
Fax: (602) 917-5256
E-Mail: [log in to unmask]
Website: http//www.rogers-corp.com/cmu
////////////////////////////
// SERVICE TO THE LINE, //
// ON THE LINE, //
// ON TIME. //
////////////////////////////
______________________________ Forward Header
__________________________________
Subject: corrosion
Author: Christer.Marklund::(CHRSTR) at ~FABRIK
Date: 2/27/97 4:50 AM
From: [log in to unmask]
Date: Thu, Feb 27, 1997 4:50 AM
Subject: corrosion
To: Andrew P Magee; TechNet
----------
Received: from 168.113.24.64 by post.fabrik.com
with SMTP (Fabrik F07.0-000)
id [log in to unmask] ; Thu, 27 Feb 1997 07:33:48 -0800
Received: from ipc.org by simon.ipc.org via SMTP (940816.SGI.8.6.9/940406.SGI)
id JAA06874; Thu, 27 Feb 1997 09:02:29 -0800
Resent-Date: Thu, 27 Feb 1997 09:02:29 -0800
Received: by ipc.org (Smail3.1.28.1 #2)
id m0w06Zv-00080UC; Thu, 27 Feb 97 08:12 CST
Resent-Sender: [log in to unmask]
Old-Return-Path: <[log in to unmask]>
From: [log in to unmask]
X-Openmail-Hops: 1
Date: Thu, 27 Feb 97 13:50:36 +0100
Message-Id: <H000032400ba5029@MHS>
Subject: corrosion
Mime-Version: 1.0
To: [log in to unmask]
Content-Type: multipart/mixed; boundary="openmail-part-00d50fff-00000001"
Resent-Message-ID: <"MCU_w3.0.ApC.XPP5p"@ipc>
Resent-From: [log in to unmask]
X-Mailing-List: <[log in to unmask]> archive/latest/10723
X-Loop: [log in to unmask]
Precedence: list
Resent-Sender: [log in to unmask]
----------
Date: Mon, 24 Feb 97 15:55:30 +0100
Content-Type: message/rfc822
----------
---------------------------- Forwarded with Changes ---------------------------
From: Christer.Marklund::(CHRSTR) at ~FABRIK
Date: 2/27/97 4:50AM -0800
To: Andrew P Magee at Rogers-MCD
*To: TECHNT at ~FABRIK
Subject: corrosion
-------------------------------------------------------------------------------
Subject: corrosion
MIME-Version: 1.0
From: [log in to unmask]
TO: [log in to unmask]
Content-Type: multipart/Mixed; boundary="openmail-part-00d50fff-00000002"
--openmail-part-00d50fff-00000002
Content-Type: text/plain; charset=US-ASCII; name="corrosion"
Content-Disposition: inline; filename="corrosion"
Content-Transfer-Encoding: 7bit
Dear technetters.
A few days ago i asked You a question about stainless steel of type 303.
We had some problem soldering a nickel plated stainless connector to
ceramic. As many of You mentioned the problem with that soldering was a
material in the connector that didn`t match the ceramic.
The connector supplier will change to kovar or some other material with
coefficient of thermal expansion at 10-11 ppm or lower.
A new question:
I sometimes come into contact with galvanic corrosion at different
moisture tests.
We normally use a lot of aluminium in our designs. Aluminium in contact
to other material (nickel, gold etc) in severe environments will make
corrosion damages to the aluminium.
The potential for different material (EMF) could be found in different
litteratures.
Aluminium is normally given a potential of -0.6 to -0.8 V depending of
alloy type.
Stainless steel is about -0.35 V, nickel is about -0.15 V.
A rule of thumb is that the difference between two materials that is in
contact to each other shall not be more than 0.25 V in severe
environment.
My question is: Do any of You have any value of how much the potential
of aluminium is raised when the aluminium is chromated?
We normally use a cromate that gives a color to the aluminium surface of
golden to tan.
Regards
Christer Marklund
--openmail-part-00d50fff-00000002--
|
|
|