I would be interested in knowing which "ENTEK" broke down with the apparent
hot spots.
You mentioned anti-ox, this would suggest ENTEK CU-56, a monomolecular
coating which will break down at temperatures above 170F. ENTEK PLUS CU-106A
is a more robust coating which can pass through several thermal cycles.
Please clarify.
Tom Eshelman
Enthone-OMI
[log in to unmask]
|
|
|