Hi Dave,
To have s shiny joint, I mean very shiny joint is the customer's
requirement. I understand that gold will influence the surface texture, but
not the customers.
They follow strictly the very old thinking that appearance define
reliability and good solder joint.
Anyway, I am still cracking my head on resolving this issue.
Thanks.
Poh
At 08:21 AM 2/27/03 -0600, Dave Hillman wrote:
>Hi Poh! I just have to ask the question - "Why do you want a shiny solder
>joint"? A solder joint's surface texture has very little to do with its
>quality and use environment integrity. The JSTD-001 and 610 committees have
>acknowledged that fact with the elimination of requiring solder joints be
>"bright and shiny". Certain metallizations (such as gold) can influence the
>solder joint surface texture but have no impact of reliability. Reliance on
>a solder joint's appearance as a measure of qualify can be a dangerous
>assumption.
>
>Dave Hillman
>Rockwell Collins
>[log in to unmask]
>
>
>
> Poh Kong Hui
> <[log in to unmask] To: [log in to unmask]
> M.SG> cc:
> Sent by: TechNet Subject: [TN] : Shining
smooth solder joint on ENIG or Gold plating Board.
> <[log in to unmask]>
>
>
> 02/27/2003 06:18
> AM
> Please respond to
> "TechNet E-Mail
> Forum."; Please
> respond to Poh
> Kong Hui
>
>
>
>
>
>
>Hi Technetters,
>
>Can someone advise me how to get a good smooth shining solder joint on the
>ENIG board or board with gold plate SMT pads.
>
>As I can understand that board subjected to reflow soldering, the solder
>joint tends to look dull and not so smooth joint. But, is there any way to
>get a good shining joint.
>
>Thanks.
>
>Poh
>
>---------------------------------------------------
>Technet Mail List provided as a free service by IPC using LISTSERV 1.8e
>To unsubscribe, send a message to [log in to unmask] with following text in
>the BODY (NOT the subject field): SIGNOFF Technet
>To temporarily halt or (re-start) delivery of Technet send e-mail to
>[log in to unmask]: SET Technet NOMAIL or (MAIL)
>To receive ONE mailing per day of all the posts: send e-mail to
>[log in to unmask]: SET Technet Digest
>Search the archives of previous posts at: http://listserv.ipc.org/archives
>Please visit IPC web site http://www.ipc.org/html/forum.htm for additional
>information, or contact Keach Sasamori at [log in to unmask] or 847-509-9700
>ext.5315
> -----------------------------------------------------
>
>---------------------------------------------------
>Technet Mail List provided as a free service by IPC using LISTSERV 1.8e
>To unsubscribe, send a message to [log in to unmask] with following text in
>the BODY (NOT the subject field): SIGNOFF Technet
>To temporarily halt or (re-start) delivery of Technet send e-mail to
[log in to unmask]: SET Technet NOMAIL or (MAIL)
>To receive ONE mailing per day of all the posts: send e-mail to
[log in to unmask]: SET Technet Digest
>Search the archives of previous posts at: http://listserv.ipc.org/archives
>Please visit IPC web site http://www.ipc.org/html/forum.htm for additional
>information, or contact Keach Sasamori at [log in to unmask] or 847-509-9700
ext.5315
>-----------------------------------------------------
>
---------------------------------------------------
Technet Mail List provided as a free service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/html/forum.htm for additional
information, or contact Keach Sasamori at [log in to unmask] or 847-509-9700 ext.5315
-----------------------------------------------------
|
|
|