I introduced Tefzel as being a wire and connector specialist, but it's so long back that my poor cells have forgotten most, however, as far as figure it out, the change from Teflon to Tefzel was the considerable price difference. We never had Tefzel cold-flow problems in our MIL equipments.
Best wishes
Ingemar
Dear Technet friends,
We've been using tefzel (a modified teflon) insulated wires in our transformer
assemblies. Some people are concerned that the teflon's cold-flow property would
end up in shorts between windings where there are pressure points. My questions
are:
- Is tefzel better than the unmodified teflon in this respect?
- How is the cold-flow characteristic quantified?
- Where can I find the "cold-flow index" of the materials?
Yours sincerely
K.K. Chin
Artesyn Technologies
Fremont, CA
##############################################################
TechNet Mail List provided as a free service by IPC using LISTSERV 1.8c
##############################################################
To subscribe/unsubscribe, send a message to [log in to unmask] with following text in
the body:
To subscribe: SUBSCRIBE TECHNET <your full name>
To unsubscribe: SIGNOFF TECHNET
##############################################################
Please visit IPC web site (http://www.ipc.org/html/forum.htm) for additional
information.
If you need assistance - contact Gayatri Sardeshpande at [log in to unmask] or
847-509-9700 ext.5365
##############################################################
|
|
|