Re: Tin Coatings
From:
Paul Gould <[log in to unmask]>
Date:
Sun, 5 Jan 1997 13:19:02 +0000
Content-Type:
text/plain
Parts/Attachments:
text/plain (23 lines) 
In message Oscar Cammuse writes
>
>Does anyone have experience with Sn coatings on boards in lieu of solder
>coatings and OSP coating?  What problems have you experienced?  Why is Sn
>coatings not so acceptable?
>
We have used immersion tin coatings which are very thin and these have a very
short shelf life of less than 2 weeks before solderability is unacceptable.
-- 
Paul Gould

***************************************************************************
* TechNet mail list is provided as a service by IPC using SmartList v3.05 *
***************************************************************************
* To unsubscribe from this list at any time, send a message to:           *
* [log in to unmask] with <subject: unsubscribe> and no text.        *
***************************************************************************
* If you are having a problem with the IPC TechNet forum please contact   *
* Dmitriy Sklyar at 847-509-9700 ext. 311 or email at [log in to unmask]      *
***************************************************************************

ATOM RSS1 RSS2