Hello Sakamoto,

Do you have more detailed information which is able to share, say,
stress-strain curve at different temp, creep property, chemical composition
percentage of two alloys?

Thanks in advance.

Han JiangBo

-----Original Message-----
From: <Ichi $B!! (Bsakamoto>
[mailto:[log in to unmask]]
Sent: Friday, April 28, 2000 6:23 PM
To: [log in to unmask]
Subject: [LF] Material Properties





Dear Quadir
SnAgCu is 29MPa.
SnCu is 21MPa.
Thanks
----------------------  $BE>Aw<T (B: ichizo sakamoto/OMRONJP  $BE>AwF| (B:
2000/04/28 20:20
---------------------------


Yasir Abdul Quadir <[log in to unmask]> on 2000/04/28 18:59:49
 $BAw?.<T (B:  Yasir Abdul Quadir <[log in to unmask]>

"Leadfree Electronics Assembly E-Mail Forum." <[log in to unmask]>
$B$KJV?.$7$F$/$@$5 (B
       $B$$ (B; [log in to unmask] $B$KJV?.$7$F$/$@$5$$ (B


 $B08@h (B: [log in to unmask]
cc:    (bcc: ichizo sakamoto/OMRONJP)
 $B7oL> (B: [LF] Material Properties

################################################################
Leadfree E-Mail Forum provided as a free service by IPC using LISTSERV 1.8c
################################################################
To subscribe/unsubscribe, send a message to [log in to unmask]
with following text in the body:
To subscribe:   SUBSCRIBE Leadfree <your full name>
To unsubscribe:   SIGNOFF Leadfree
###############################################################
Please visit IPC's Center for Lead-Free Electronics Assembly
(http://www.leadfree.org ) for additional information.
For technical support contact Keach Sasamori [log in to unmask] or 847-790-5315.
################################################################