Subject:
Re: 96.5% Tin / 3.5% Silver vs. SAC305
From:
MA/NY DDave <[log in to unmask]>
Reply To:
(Leadfree Electronics Assembly Forum)
Date:
Wed, 3 Aug 2005 13:37:38 -0500
Content-Type:
text/plain
Parts/Attachments:
text/plain (19 lines) 
Hi KEDS-Rich, John, SPVC, IPC LF Listservers

Stopping for a minute on this fun discussion/learning experience.

If you decide to use 96.5Sn you do know that your soldering temperature
will be higher and you might have component MSL problems. I know it is only
a few degrees yet you don't have lots of margin on some of your products.


YiEngr, MA/NY DDave

-------------------------------------------------------------------------------Leadfee Mail List provided as a service by IPC using LISTSERV 1.8d
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Leadfree
To temporarily stop/(start) delivery of Leadree for vacation breaks send: SET Leadfree NOMAIL/(MAIL)
Search previous postings at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-------------------------------------------------------------------------------

ATOM RSS1 RSS2